VHB Acrylic Foam Tape is a powerful, double-coated adhesive engineered for bonding diverse substrates, including low surface energy plastics and metals. This technical guide details its superior performance characteristics, covering high tensile/shear strength, moisture resistance, and suitability for challenging industrial environments. Industrial professionals seeking robust solutions to replace permanent fasteners like rivets or spot welds will find this indispensable resource for reliable joining systems in both exterior and interior applications.
Page 1 Text Content
VHB Acrylic Foam Tape 5952F
Product Data Sheet
Updated : Sept 2002 Supersedes New
Product Description 3M VHB Acrylic Foam Tape 5952 is a double coated pressure sensitive adhesive tape for bonding a wide variety of substrates including lower surface energy materials such as powder coated paints and plastics.
In many cases abrasion of surface is not required.
Physical Properties Adhesive Type Acrylic Foam.
Not for specification purposes
Thickness (ASTM D-3652) 1.1 mm
Foam Density 590 kg/m³
Release Liner Red polyethylene film
Tape Colour Black
Shelf Life 24 months from date of manufacture by 3M (when stored in original cartons at 20°C & 50 % Relative Humidity)
Performance Peel Adhesion to
Characteristics Stainless Steel 35 N/10mm
90° peel @ room temp, 72 hr dwell,
Not for specification purposes
jaw speed 300mm/min
Static Shear Strength weight held for 10,000 mins to stainless steel
with ½ sq in (3.23 sq cm) overlap
Normal Tensile (T-
Block) 620 k Pa
to Aluminium at room temp, 6.45 sq cm, jaw speed 50 mm/min
Temperature Performance
(Minutes/Hours) °C (Days/Weeks) °C
Solvent Resistance High
Splash testing cycle - 20 seconds submersion - 3 cycles.
UV Light Resistance Excellent.
Page Summary Contents For 3M VHB Acrylic Foam Tape 5952F User's Manual
Manual Details
| Brand | 3M |
|---|---|
| Pages | 2 |
| File Size | 42.29 KB |
| Published | May 12, 2026 |
Enter the captcha to get the download link:
Frequently Asked Questions
How do I prepare surfaces for the best bond strength?
Surfaces must be clean, dry, and unified. For optimal adhesion, firm application pressure must be used during installation.
What preparation is needed for different types of materials?
Porous materials (like wood) need sealing while metals like copper or brass require priming or coating to prevent interaction with the adhesive.
Can this tape bond effectively to all plastics?
No; it can be problematic with low surface energy materials such as polyethylene, polypropylene, PTFE, and silicones. Thorough evaluation is recommended.
What safety precautions must I take when cleaning substrates?
Users must take proper safety precautions when handling suggested solvents like isopropyl alcohol or heptane.